Appl. Phys. Lett. 82, 3901 (2003)
E. M. Kaidashev, M. Lorenz, H. von Wenckstern, A. Rahm, H.-C. Semmelhack, K.-H. Han, G. Benndorf, C. Bundesmann, H. Hochmuth, and M. Grundmann
Abstract
A multistep pulsed-laser deposition (PLD) process is presented for epitaxial, nominally undoped ZnO thin films of total thickness of 1 to 2 μm on c-plane sapphire substrates. We obtain reproducibly high electron mobilities from 115 up to 155 cm2/V s at 300 K in a narrow carrier concentration range from 2 to 5×1016 cm−3. The key issue of the multistep PLD process is the insertion of 30-nm-thin ZnO relaxation layers deposited at reduced substrate temperature. The high-mobility samples show atomically flat surface structure with grain size of about 0.5–1 μm, whereas the surfaces of low-mobility films consist of clearly resolved hexagonally faceted columnar grains of only 200-nm size, as shown by atomic force microscopy. Structurally optimized PLD ZnO thin films show narrow high-resolution x-ray diffraction peak widths of the ZnO(0002) ω- and 2Θ-scans as low as 151 and 43 arcsec, respectively, and narrow photoluminescence linewidths of donor-bound excitons of 1.7 meV at 2 K.